1. TAA Low Carbon Bainite Steel Shot
2. Save 50% shot blasting cost !
3. Longer lasting and more durable
Low Carbon Bainite Steel Shot
---- save 50% of the shot blasting cost !
a) High strength, high ductility, long service life;
b) Low breakage, low wear, little dust;
c) Low wear of the equipment, long life of accessory;
d) Reduce dedusting system load, lengthen usage time of dedustig equipments.
Description:
TAA high quality LCB Steel Shot is a newly developed product, which spend decade long efforts of TAA technician team. After being put into use in many foundries, the result shows that TAA high quality abrasive ---- LCB Steel Shot could help to save 50% of shot blasting cost compared with common steel shot.
Specification
Item | Low Carbon Bainite Steel Shot | |
Chemical Composition | C | 0.08% - 0.20% |
Si | 0.10% - 0.25% | |
Mn | 0.35% -1.50% | |
S | ≤0.030% | |
P | ≤0.030% | |
other alloy element | Cr, Mo, Ni, B, Al, Cu | |
Hardness | HRC 40-56 | |
Metallographic Structure | Duplex structure combined martensite and bainite |
Note:
1. Keep harmful element content under 0.03% to increase tenacity and lengthen service life;
2. Adding alloy element to make it possess the excellent property of alloy steel;
3. Proper hardness ensure the shot blast efficiency;
4. Duplex structure can ensure high ductility and high strength.
From the above Fatigue Life test, we can tell that the residual amount after impacted 500 times is respectively 70%, 40% and 20% for Low Carbon Bainite Steel Shot, common low carbon steel shot and high carbon steel shot. Low Carbon Bainite steel shot is competitively priced compared with common steel shot due to its low wear and long service life.
In addition, TAA Low Carbon Bainite Steel Shot is suitable for all the fields that use common steel shot.