Impregnation Adhesives for Carbon Fibre
1.Modified epoxy resin
2.Good penetration
3.Low viscosity
4.Water resistance
HM-180C3P Modified Epoxy Resin Carbon Fiber Impregnation Adhesive is used for impregnation and paste of reinforced component surface and fiber products.
It is completely impregnated in fiber products, and coheres fiber products effectively with the component surface, thereby to strengthen the components.
1. Product Characteristics
1) Good compatibility with carbon fiber.
2) Aging, water resistance and chemical corrosion resistance, excellent performance.
3) Low viscosity, can completely impregnated in fiber products.
4) The adhesive layer has excellent physical mechanical properties after curing, such as strong toughness and elasticity.
2. Application Range
This product is epoxy fiber adhesive of high performance, which is mainly used for the strengthening and reinforcement of buildings.
It can be used for the effective penetration bonding between many substrate materials and many fiber fabrics.
Substrates can be concrete, steel material, ceramic, stone, wood component, etc.
Fiber products can be carbon fiber, glass fiber, basalt fiber, aramid fiber, etc.
3. Working Performance
Slump (40°C) | 2.0 mm |
Operable Time (40°C) | > 60 min |
Applicable Temperature | 5 ~ 40 °C |
4. Colloidal Performance
Compressive Strength | ≥ 70.0 MPa |
Tensile Strength | ≥ 40.0 MPa |
Bending Strength | ≥ 50.0 MPa |
Elastic Strength | ≥ 2500 MPa |
5. Bonding Capacity
Steel–steel Tensile Shear Strength | ≥ 14 MPa |
Pulling Bonding Strength along with Concrete | ≥ 2.5 MPa |
6. Usage Amount
The usage amount is 0.6-0.9 kg for a square meter of fiber cloth.
7. Package
30 kilograms per set. A net: 20 kilograms (Nor.) B net: 10 kilograms (Nor.)
Other packing weight is optional according to customer's requests.