OPC 42.5N/R according to BS 12/96 or ASTM C-150 or CE-197, SABS, BIS, GB175-1999 and so on.
SPECIFICATIONS ARE AS FOLLOWS
GREY PORTLAND CEMENT FOR CONSTRUCTION GRADE 42.5 ACCORDING TO BRITISH AND EN 197-1/2000 OR ASTM C 150
Chemical Composition
SILICON DIOXIDE (SIO2) 20.08 - 21.50
ALUMINIUM OXIDE (A12O3) 5.30
FERRIC OXIDE (FE2O3) 3.25 3.50
CALCIUM OXIDE (CAO) 65.60
MAGNESIUM OXIDE (MGO) 1.70 3.00
SULPHUR TRIOXIDE (SO3) 2.70 3.00
LOSS OF IGNITION (LOI) 1.80 3.00
INSOLUBLE RESIDUE % 0.1 0.7
TRICALCIUM SILICATE (C3S) 50.00 54.40
DICALCIUM SILICATE (C2S) 14.2 18.20
TRICALCIUM ALUMINATE (C3A) 6.00 6.80
TRICALCIUM ALUMINO FERRICE (C4AF) 11.60
CHROMIUM (CR%) 2.0 MAX
Physical and Mechanical Properties
BLAIN CM2/GR 3.250
AUTOCLAVE EXPANTION 0.02
NORMAL CONSISTENCY % 27.5
INITIAL SETTING TIME (VICAT)(HOURS-MINS) 3.25-4.50
HARD SET (HOURS-MINS) 4.54 6.00
FITNESS INDEX (CM2/GM) 2800-3040
COMPRESSIVE STRENGTH ISO/EN 197-1/2000 BS 4550 MORTAR
@ 03 DAYS 2.65 34.2 KG/CM2
@ 07 DAYS 37.3 42.5 KG/CM2
@ 28 DAYS 52.8 54.6 KG/CM2
British Standard Clinker
EXAMINE ITEM GUARANTEED
CAO 64%MIN
SIO2 20.0-23.0%
AL2O3 4.0-5.5%
FE2O3 2.0-3.5%
MGO 3.3-4.5%
SO3 1.0%MAX
LOSS OF IGNITION 1.5%MAX
F-CAO 1.5%MAX
INSOLUBLE RESIDUE 0.75%MAX
(NA2O+0.65K2O) 0.60%MAX
C3S 50-65%