Calcium aluminate Cement
The goods has execllent high-temperature service
supply calcium aluminate cement
(CA50,CA-70,CA-80)
Calcium aluminate Cement
chemical composition
characteristic Al203 SiO2 Fe203 R2O S(total sulfur) C
CA500 50%-60% 8%Max 0.4%Max 0.1*Max 0.1%*Max
A500 50%-60% 8%Max 0.4%Max ----- ------
physical property
charateristic A700 A900 A600
Time of setting
initial setting time H:MIN 0:30min 1:00min 0:30min 0:30min
final setting time H:MIN 6:00max 6:00max 6:00max 6:00max
compression strength
1d MPa 52min 72min 45min 40min 40min
3d MPa 62min 82min 55min 50min 50min
Chemical Composition
name Al2O3 CaO SiO2 Fe2O3 TiO2 MgO
A 36 45-48 ≤3.5 ≤1.5 ≤1.8 ≤1.0
B 38-41 47-50 ≤4.0 ≤2.0 ≤2.0 ≤1.0