China Competitive Fireproof Boards
Ceramic fiber blanket
Ceramic fiber paper
Cermaic fiber board
Fireproof Boards With Carton Packing
Refractory Ceramic Fiber Boards For Furnace Construction , we can produce many kinds of ceramic fiber products, such as ceramic fiber blanket, board, module etc. we are very specialized and competitive in this line.
Characteristic:
Low thermal conductivity , low thermal capacity,and excellent thermal insulation property.
High temperature stability ,resistance to thermal shock
Good tensile strength
Excellent sound absorption, fire protection and chemical corrosion resistance.
Application:
Mainly serve as the ceramic fiber lining for industrial furnaces, heating equipment and high- temperature pipelines,such as
Metallurgy Industry: heating furnaces,heat treatment furnaces and ladle insulated cover
Mechanism industry: thermal insulation material for electric power boilers, gas turbine engine and nuclear power plant
Tech Data
| Standard | High Pure | High Aluminum | Zirconium | |
Classifition temperature(oC) | 1260 | 1260 | 1360 | 1430 | |
Work temperature(oC) | 1050 | 1100 | 1200 | 1350 | |
Color | Pure white | Pure white | Pure white | Pure white | |
Density(kg/m3) | 280 | 280 | 280 | 280 | |
480 | 480 | 480 | 480 | ||
Permanent linear shrinkage(%) (after24hours,density320kg/m3) | -3 | -3 | -3 | -3 | |
(1000oC) | (1100oC) | (1200oC) | (1350oC) | ||
Thermal conductivity(w/m.k) density285kg/m3) | 0.085(400oC) | 0.085(400oC) | 0.085(400oC) | 0.085(400oC) | |
0.132(800oC) | 0.132(800oC) | 0.132(800oC) | 0.132(800oC) | ||
0.180(1000oC) | 0.180(1000oC) | 0.180(1000oC) | 0.180(1000oC) | ||
Compressive strength (Mpa) (thermal shrinkage 10%) | 0.5 | 0.5 | 0.5 | 0.5 | |
Chemical composition (%) | AL2O3 | 46 | 47-49 | 52-55 | 39-40 |
AL2O3+SIO2 | 97 | 99 | 99 | - | |
AL2O3+SIO2+Zro2 | - | - | - | 99 | |
Zro2 | - | - | - | 15-17 | |
Fe2O3 | <1.0 | 0.2 | 0.2 | 0.2 | |
Na2O+K2O | ≤0.5 | 0.2 | 0.2 | 0.2 | |
Size (mm) | 1200x1000; 1200x600; 1000X1000, 900x600; 600x300 | ||||
Thickness | 10-80mm | ||||