Heat insulation material ceramic fiber blanket 1400C, China Heat insulation material ceramic fiber blanket 1400C Supplier,Factory

Heat insulation material ceramic fiber blanket 1400C

Zibo Jiuqiang Refractory Co., Ltd. [China]

Minimum Order: 0

Quality/Safety Certification: 0.00

Heat insulation material ceramic fiber blanket
Tylpe:1000C/1100C/1260C/1360C
Density:96-160kg/m3
Thickness:20-50mm

Heat insulation material ceramic fiber blanket

Tylpe:1000C/1100C/1260C/1360C
Density:96-160kg/m3
Thickness:20-50mm

Jiuqiang Ceramic Fiber heat insulation blanket is made of special ceramic long-fiber that is produced by the melting of very pure raw materials in double surface meeding process with out binders and with good stability in a large range of temperature. The process of double surface needing increase interweaving and tensile strength. Its unique fiber layup and needling process provide Jiuqiang Ceramic Fibre Blanket with outstanding consistency, handling strength and resiliency at elevated temperatures

Applications

1.Industrial insulating,sealing and protecting materials

2.Fiber composite (for example: grinding parcel)

3.Internal and external lining for industrial furnace

4.Structure refractory and sponging sounds

5.Materials for hot filtration

6.Raw materials for further producing

7.Technical Specifications

8.Joint sealing and filling insulation (kiln car, pipeline, kiln door and so on)

Characteristics

1.Excellent thermal stability

2.Excellent chemistry quality

3.Resistance to burning

4.Low thermal conductivity

5.Low heat storage

6.Low shrinkage

7.Good obstructing voice and mechanism strength

8.Good springiness for fibersConvenient producing and installing

Technical Specifications

Type		Ordinary	Standard	High Purity	High Aluminium	Zirconia
Classification temperature (°C)		1100	1260	1260	1360	1430
Working Temperature (°C)		< 1000	1050	1100	1200	1350
Color		white	spotlessly white	spotlessly white	spotlessly white	spotlessly white
Density (kg/m3)		96 128	96 128	96 128	128 160	128 160
Shrinkage on heating (%) (24 hours,density as 128/m3)		-4 (1000°C)	-3 (1000°C)	-3 (1100°C)	-3 (1250°C)	-3 (1350°C)
Thermal conductivity by different temperature (w/m.k) (density as 128kg/m3)		0.09(400°C) 0.16(800°C)	0.09(400°C) 0.16(800°C)	0.09(400°C) 0.16(800°C) 0.20(1000°C)	0.12(600°C) 0.20(1000°C)	0.16(800°C) 0.20(1000°C)
Tensile strength (MPa) (density as 128kg/m3)		0.04	0.04	0.04	0.04	0.04
Chemical composition (%)	AL2O3	44	46	47-49	52-55	39-40
	AL2O3+SIO2	96	97	99	99	-
	AL2O3+SIO2+ZrO2	-	-	-	-	99
	ZrO2	-	-	-	-	15-17
	Fe2O3	<1.2	<1.0	0.2	0.2	0.2
	Na2O+K2O	≤0.5	≤0.5	0.2	0.2	0.2
Size (mm)		Spec. 7200×610×10-50 Other sizes can be available.