Naphthalene Sulfonate formaldehyde condensate
(NSF-A 5%NaSO4)
Detailed Product Description
1.Remarkable Plasticity: As a condition of blending where amount of cement and collapsibility are fixed aforehand, mixing water can be decreased by 18-28% when it is admixed with reinforced concrete at 0.5-1.0%. Statistically, compression strength on the lst day, the 3 rd day and the 28 th day after single application is increased by 60-90% and 25-60% respectively when it is added at standard blend dosage. As the result, compression strength, tensile strength, buckling strength and modulus of elasticity will be improved to some extent.
2. Improve miscibility of concrete amalgamator with water and collapsibility as well. As a condition of equivalent blending, collapsibility can be increased 5-8 times when it is added at 0.7% blend dosage.
3. 15-20% of cement can be reserved when the agent is blended at 0.7% blend dosage, which is preconditioned by same collapsibility and strength.
PARAMETERS & ACCEPTANCE CRITERLA
model item | NSF-A |
net starch fluidity (mm ) | ≥ 240 |
content of Cl (%) | 0.3 |
PH value | 7 9 |
surface tension(N/m) | (7 1 ± 1) × 10 -3 |
solids content(%) | ≥ 92 |
Na 2 SO 4 content(%) | ≤5 |
PARAMETERS & ACCEPTANCE CRITERIA FOR REFERENCE
Parameters
Criteria
Actual Results
Parameters
Criteria
Actual Results
Water Reduction, %
≥ 18
21.8
Compression strength, %
1d
≥ 180
200
Water Penetration, %
≤ 90
79
3d
≥ 170
194
Air Content, %
≤ 2.0
1.6
7d
≥ 150
161
Temporal Distribution for setting (min)
Initial setting time
-9 0 +120
+20
28d
≥ 130
142
Terminal setting time
+13
Shrinkage, %
28d
≤ 130
125
Corrosion to steel bars
None
None
Note: Standard Blend Dosage:0.7 %(as cement amount)