1. Material : 70%wood powder, 20%PVC and 10% additives
2.Optional Color: white,river gum,iron box,mahogany etc
we can offer this below lesco wood:
Size:95mm*13mm,137mm*20mm,150mm*11mm,197mm*16mm,
195mm*30mm,150mm*16mm and you request.
LESCO Material
| Lesco wood composite material is a small amount plastic plastic and wood waste from the synthetic polymer powder timber is artificial wood. As the product mixed with a small amount plastic components, can effectively remove the natural defects of natural wood ,can nails, drilling, grinding, sawing, planing, paint, not easy to deformation, Unique production process and technology ,can make the loss of raw materials reduced to zero. | |||
Optional Color | white,river gum,iron box,mahogany etc. | |||
Material | 70%wood powder, 20%PVC and 10% additives | |||
Surface | burnished(smooth), grooved, serrated,embossing etc | |||
Applications | office, hotels, public buildings, superstores, architectural fascias, commercial premises | |||
Advantages | 1.weathering-resistant No change in characteristics after exposure to sunlight,rain and temperature. 2.insect-resistant The special stuucture of wood power and PVC keeps the termite away. 3.flame-retardant With PVC material inside,Lesco wood products are flame retardant if there's no naked fire. 4.environment-friendly Wood power takes up 70%.The amount of formaldehyde and benzene released from Lesco wood products is far below the national and European standards,which will do not harm to human body. 5.water-proof Low water absorption rate,suitable for wet environment 6.recyclable The products could be recycled and used again. | |||
PROPERTIES | TEST STANDARD | TEST RESULT | ||
DECKING | CLADDING | |||
Bending Strength | ASTM D103-93 | 27.4N/mm2 | 1437 MPa | |
Crack Strength | ASTM D103-93 | 37MPa | 23 MPa | |
Moisture Content | ASTM D648 | 1.7% | ||
Water Absorption | ASTM D648 | 1.74% | ||
The Size Change Rate After Heating | GB/T 8814-1998 | ±2% | ||
The Size Change Rate After Different Temperature | GB/T 8814-1998 | ±0.2% | ||
Wearability | GB/T 8814-1998 | ≤0.08g/100r | —— | |
Vicat Softening Temperature | ASTM D648 | 83°C | ||
Fire Retardant | UL-94 : 1991 | 94V-0 | ||
Durability | 1200h ASTM 790/BS E6 | No change in performance | ||
Color fastness | AATCC 16E | ≥class 4.0 | ||
Formaldehyde Release | GB 18580-2001 | ≤0.2mg/L | ||
Lead & Heavy Metal Content (ppm.max) | GB 18580-2001 | ≤10ppm | ||
Specific Density |
| 850kg/m3 | 750kg/m3 |