1. Material: nitinol
2. Composition: Ni-51@%-Ti
3. Application: dental implant
4.Size:0.1mm-1.0mm
Diameter (mm) | 0.025--1±0.075 1—2.5±0.00127 2.5—4.4±0.025 |
Mechanical treatments | --Cold drawn --Superelastic --Trained |
Surface finish | --Hard dark Oxide --Dark Oxide --Drawn Bright --Pickled --Mechanically or electro-polished |
Typical impurity content in wt | O<250ppm C<250ppm Total all others<1000ppm |
Standard Cut-length | ±0.18mm for L<0.3m |
Tolerances Formats | ±0.2% of specified cut-length for L<0.3m Round, Square, Rectangular, Shaped wire |
(1) Upon Request Note: Refer to specifications for torqueability & straightness, Burr-free or sheer-cut available. |
As(Fully annealed) | Af<35 |
Nominal Loading plateau stress@3% strain, in Austenite | 294 Mpa 42,500psi |
Nominal Ultimate Tensile Strength in Austenite | 1053Mpa 152,500psi |
Max.Residual elongation after 8% strain in Austenite (%) | 0.5 |
Min.elongation to failure in Austenite | 10 |
Main Applications | Implantable devices Stents |