Fiberglass Woven Roving.
Density (g/m2): 200/260/300/360/400/500/570/600/800
Width (mm): 70-2600
Fiberglass Woven Roving is bidirectional fabric made by interweaving direct roving.
Woven Roving are compatible with many resin systems such as polyester, vinyl ester, epoxy and phenolic resins. Woven Roving are high-performance reinforcement widely used in hand lay-up and robot processes for the production of boats, vessels, plane and automotive parts, Pipe, furniture and sports facilities.
General Data.
Product Code: EWR & CWR.
Density (g/m2): 200/260/300/360/400/500/570/600/800
Roll Width: 200mm-1270mm. Usually is 1000mm/1270mm
Roll Weight: 30-60kgs
Package: Product is manufacture in form of a roll wrap on a paper tube then after packed in a plastic bag and placed with in a cardboard carton. Rolls can be loaded in a container directly or on pallets.
Deposited: It should be stored in dry, cool, clean and rainproof area. Recommended temperature range of storage is between 15-30 and relative humidity between 35%-70%,
| TECHNICAL CHARACTERISTICS (nominal values) | |||||||||
| Serial No. | Product No. | Glass Type | Warp /Weft Tex | Warp Density Ends/cm | Weft Density Ends/cm | Area Weight g/m2 | Pattern | Standard Width | |
| 1 | EWR200 | E | 180/180 | 6.00 | 5.00 | 200 | Plain | 1000 | 1250 |
| 2 | EWR260 | E | 300/300 | 4.60 | 4.10 | 260 | Plain | 1000 | 1250 |
| 3 | EWR300 | E | 300/380 | 5.00 | 4.00 | 300 | Plain | 1000 | 1250 |
| 4 | EWR360 | E | 600/900 | 3.20 | 1.80 | 360 | Plain | 1000 | 1250 |
| 5 | EWR500 | E | 1200/1200 | 2.20 | 2.00 | 500 | Plain | 1000 | 1250 |
| 6 | EWR600 | E | 1200/1200 | 2.60 | 2.50 | 600 | Plain | 1000 | 1250 |
| 7 | EWR800 | E | 2400 | 1.80 | 1.80 | 800 | Plain | 1000 | 1250 |
| Other specifications are available in customer request. | |||||||||
| TECHNICAL PARAMETERS | |||||||||
| Area Weight (%) | Moisture(%) | Combustible (%) | Warp and weft density(%) | Width (Max.) | |||||
| ISO 3374 | ISO 3344 | ISO 1887 | ISO 4602 | ISO 5025 | |||||
| ± 5 | ≤0.20 | 0.40-0.70 | ± 5 | ± 1% | |||||