1)FKM compounds withour carbon black;
2)Excellent heat and oil resistance;
3)Oxygen resistance;
4)stable in high quality;
Technical Data sheet
| Typical Values | |||||
Fluonine Content % | 66.0 | |||||
Specific Gravity | 1.82 | |||||
Color | wite | |||||
Mooney Viscosity ML1+10@121 | 55 | |||||
Typical Properties of | ||||||
Test Compound |
|
| ||||
Polymer |
| 100 | ||||
MT Black(N990) | Phr | 20 | ||||
MgO | Phr | 3 | ||||
Ca(OH)2 | Phr | 6 | ||||
Curing Condition | Press | 10min@170 | ||||
Oven | 16h@230 | |||||
Tensile (ASTM D412) | MPa | 14.7 | ||||
Elongation at break (ASTM D412) | % | 261 | ||||
Hardness (ASTM D2240) | Shore A | 71 | ||||
Compression Set (ASTM D395) |
|
| ||||
Method B ) 200@70h | % | 19.9 | ||||
Typical Rheological Properties Monsanto Moving Die Rheometer (MDR2000) 100cpm,0.5°Arc,6min@177 | ||||||
ML | Nm | 0.17 | ||||
MH | Nm | 1.08 | ||||
ts2 |
| 1.09 | ||||
t(90) |
| 3.33 | ||||
Highly recommended for applications like: O-rings, seals, gaskets, calendered goods, extrude tubing and so on.