epoxy compound fiberglass resin sheet
themosetting materials
66kv,400kv,33kv,100kv
insulators core rod
line cross-arms
FPR rods pultrusion process
epoxy fiber bar is made from fiberglass roving. continuous strand mat and surface mat which are impregnated with resin
Properties
NO | PARAMETER | unit | indicators |
1 | Density(20±2°C) | g/cm3 | ≥2.0 |
2 | Water Absorption rate(at 20±2°C,24h) | % | ≤0.05 |
3 | Tensile Strength | Mpa | ≥1200 |
4 | Bending Strength | Mpa | 900 |
5 | dye penetration test | min | ≥15 |
6 | water diffusion test(1% NaCI boiling for 100h, 12kv,1min) | µa | ≤200 |
7 | Volume resistivity(140°C,96h) | Ω.M | 10*1010 |
8 | DC breakdown(10min) | KV | 60kv |
9 | Lightning impulse withstand voltage(10kv,10mm) | times | 8 |
10 | Bending Strength at heating conditions | Mpa/150°C | 310 |
11 | ECR rod stress corrosion(1mo1/1HNO3,at 67%stress) | h | ≥96 |
Diameter (mm) A | Approx weight (kg/m) |
12 | 0.24 |
16 | 0.43 |
17 | 0.481 |
17.48 | 0.508 |
18 | 0.53 |
20 | 0.66 |
22 | 0.8 |
24 | 0.95 |
25 | 1.03 |
28 | 1.29 |
30 | 1.48 |
34 | 1.91 |
35 | 2.02 |
38 | 2.38 |
40 | 2.64 |
45 | 3.34 |
50 | 4.12 |
53 | 4.63 |
60 | 5.93 |
70 | 8.08 |
80 | 10.55 |
90 | 13.35 |
Item | Measurement A*B ( mm) |
1 | 10*22 |
2 | 10*30 |
3 | 14*22 |
4 | 16*22 |
5 | 16*30 |
6 | 20*40 |
7 | 20*30 |
8 | 30*50 |
9 | 40*50 |
10 | 40*60 |
11 | 50*25 |
12 | 50*50 |
13 | 60*60 |
Any items not seen there, please contact me, Thanks .