Working temperature: -200 ~ 2500 Deg.C
Tensile Strength: > 70 kgf/cm2
Compressive Strength: > 800kgf/cm2

Description: Manufactured from flexible graphite foil mechanically clinched to (0.20mm~0.25mm) thick carbon steel tanged (perforated) metal sheet -08F tinplate insert. It is best gasket material for cylinder head gasket and exhaust gasket. 

Product Date Sheet 

Density: 1.30~1.50g/cm3 

Working temperature: -200 ~ 2500 Deg.C (In Non Oxidizing Atmosphere) 

Threshold Temp for Oxidation: 500 Deg.C (a temp at which weight reduced 1% during 24 hrs in air) 

Tensile Strength: > 70 kgf/cm2 

Compressive Strength: > 800 kgf/cm2 

These are best material of cylinder head gasket and exhaust gasket.