FRP roof board is bright and clean appearance, light weight and high igh performance, high light transmittance, anti-corrosion.
SKYLITE Fireproofing Grade I (p16)
Mechanical properties: High rigid and high tenacity FRP Sheet.
Resin Ingredient: DIC FHH-1060 high quality additive fireproofing resin.
Fiber Intensity: Non-alkali, non-twist, non-glue fiberglass.
Surface Treatment: Application of Melinex301 film over both sides surface.
Reinforced Line: Tensile reinforced lines with longitudinal uniform distribution (It depends on consumers to choose voluntarily whether adding)
Fiberglass: Taishan high-quality fiberglass, the content being no less than 30%.
Unit Weight: 1800g/m² 2400g/m² 3050g/m²
Nominal Thickness: 1.2mm 1.5mm 2.0mm
Temperature resistance: -60°C to +130°C
Light Transmittance: 75%±2% (jewel blue) 53%±2% (milky white)
Anti- ultraviolet Rate: 99% (adding more than 0.25% UV absorbent)
Cracking Elongation Rate: 1.9%
Thermal Expansion Coefficient: 2.3X10-5cm/cm/°C
Thermal Conductivity: 0.18w/m.k
Warranty: 15 years
Applicable scope: steel works,blast furnace plants and other plants which have high requirements of fireproofing FRP Sheet.
FRP Base Material, Ashland Gel Coat, External Layer Melinex 301 Film, Internal Layer 301 Film
Part 1: Base material represents at least 95% of total thickness and total weight of the compound. The thickness of this layer is a decisive factor on the products strength, tenacity, anti- ageing capacity, size and shape. It is made up of 2/3 unsaturated resin, 1/3 fiberglass and a small quantity of additives. TR uses most advanced DTM-1 unsaturated resin and ultraviolet absorbent components in its materials, which makes FRP Sheet anti-ageing capable, resistant to color change, high transparency rate and long lifespan.
Part 2: External Layer Treatment. Generally, Melinex 301 provides the FRP material flexibility, protection against water decomposition and self cleaning function
Part 3: Gel coating surface.Enables protection against water decomposition, and function to absorb UV, prevent the base material from being damaged, increases the anti-corrosion ability.