Modified polymeric resins, engineering plastics, engineering plastics (PTT Series), PTT series modified polymeric resins
Modified polymeric resins, engineering plastics, engineering plastics (PTT Series), PTT series modified polymeric resins
The engineering plastics (PTT Series) include fiberglass reinforced PTT, flame retarded PTT, flame retarded & reinforced PTT.
The technical data of fiberglass reinforced PTT:
a) Tensile strength at break: >90
b) Bending strength (Mpa) ASTMD790: >160
c) Flexural modulus(Mpa) ASTMD790: >8500
d) Impact strenth/J.m-1(notch) ASTMD256: >85
e) Shrinkage ratio(%) ASTMD955: <1.0
The technical data of flame retarded PTT:
a) Tensile strength at break: >90
b) Bending strength (Mpa) ASTMD790: >170
c) Flexural modulus(Mpa) ASTMD790: >7500
d) Impact strenth/J.m-1(notch) ASTMD256: >85
e) Shrinkage ratio(%) ASTMD955: <1.0
f) Combustibility: 1.6mm Glass HB
The technical data of flame retarded & reinforced PTT:
a) Tensile strength at break: >90
b) Bending strength (Mpa) ASTMD790: >160
c) Flexural modulus(Mpa) ASTMD790: >7500
d) Impact strenth/J.m-1(notch) ASTMD256: >85
e) Shrinkage ratio(%) ASTMD955: <1.0
f) Combustibility: 1.6mm Glass HB
The applications of engineering plastics (PTT Series):
Entirely or partially substitute PET, PA series modified resin and supply excellent tenacity.