Glass fiber Reinforced PA66
High quality product.
Package: Coextruded paper bag lined with polyethylene film, 25kgs/bag.
Glass fiber Reinforced PA66
Specification
PA66-GF30 Reinforcement with 30% glass fiber;
PA66-GF45 Reinforcement with 45% glass fiber;
PA66-GF60 Reinforcement with 60% glass fiber.
Feature
High strength;
Good dimensional stability;
Strong dielectric property;
High heat resistance and stability;
High toughness.
Application
Air intake manifold; Engine cover; Machinery parts; Sports equipment.
Technical datas
Properties | ASTM | Test Condition | Unit | Specifications | ||
PA66-GF30 | PA66-GF45 | PA66-GF60 | ||||
Physical Properties | ||||||
Density | D-792 | 23°C | g/cm3 | 1.36 | 1.48 | 1.60 |
Melt Flow Index | D-1238 | 275°C/5.0Kg | g/10min | 12 | 8 | 5 |
Water Absorption | D-570 | 23°C,24hrs | % | 0.7 | 0.6 | 0.5 |
Mold Shrinkage | D-955 | 23°C | % | 0.3-0.8 | 0.2-0.6 | 0.2-0.4 |
Mechanical Properties | ||||||
Tensile Strength | D-638 | 10mm/min | MPa | 185 | 220 | 250 |
Elongation at Break | D-638 | 10mm/min | % | 10 | 8 | 5 |
Flexural Strength | D-790 | 2mm/min | MPa | 250 | 280 | 320 |
Flexural Modulus | D-790 | 2mm/min | MPa | 7500 | 10000 | 14000 |
IZOD Impact Strength notched | D-256 | 3.2mm,23°C | KJ/m2 | 14 | 15 | 16 |
Thermal Properties | ||||||
H.D.T | D-648 | 0.45MPa | °C | 258 | 258 | 258 |
Others | ||||||
Flammability | UL-94 | 1.6mm | — | HB | HB | HB |
Glass Fiber Content | — | — | % | 30 | 45 | 60 |
Characteristics | — | — | — | |||
Package: Coextruded paper bag lined with polyethylene film, net weight: 25kgs/bag.
Note: We could custom produce the product according to customers' requirements.