high strength engineering plastic modified nylon6 PA6
Minimum Order: 0
Quality/Safety Certification: 0.00
50% GF
high strength
engineering plastic
modified nylon6 PA6
| Performance | Test condition | Testing standard | Units | B2HG8P |
| Mechanical property | ||||
| Tensile strength | 5mm/min | ISO527-1/2 | Mpa | 183 |
| Elongation at break | 5mm/min 50mm/min | ISO527-1/2 | % | 4 |
| Bending modulus | 2mm/min | ISO178 | Mpa | 8500 |
| Bending strength | 2mm/min | ISO178 | Mpa | 293 |
| Charpy notched impact strength | 23°C | ISO179/leA | KJ/m2 | 20 |
| Charpy unnotched impact strength | 23°C | ISO179/leA | KJ/m2 | 90 |
| Thermal | ||||
| Melting | DSC.10K/min | ISO3146 | °C | 225 |
| Heat distortion temp. A | 1.8Mpa | ISO75 | °C | 225 |
| Heat distortion temp. B | 0.45Mpa | ISO75 | °C | 235 |
| Electrical property | ||||
| Surface resistivity | IEC60093 | Ohm | 1/0.1 | |
| Volume resistivity | IEC60093 | Ohm×cm | 10/0.1 | |
| Anti-arc-track of | TestotutionA | IEC60012 | V | |
| Physical property | ||||
| Density | 23°C | ISO1183 | g/cm3 | 0.7 |
| Hygroscopicity | 23°C,50%r.h | ISO62 | % | |
| Absorbent/water absorption | 23°C /saturtion | ISO62 | % | |
| Radial shrinkage | flow | ISO294-4 | % | |
| Transverse shrinkage | transverse | ISO294-4 | % | |
| Flame retardant | ||||
| Flammability test | 1.6/3.0mm | HB | ||
| The level of flame-retardant test | 1mm thickness | UL94 | ||
| Material description | PA6+40%GF High strength | |||
the color is nature, but we can supply colorful products match your requirements.