1.Tough film, wear-resisting,good adhesion
2.Excellent water resistance and anti-corrosion properties
3.Long-term protectio

A, composition and characteristics:

         by epoxy resin, asphalt, antirust pigments, char thickening agent and curing agent in the two cans of paint. Tough film, wear-resisting, high adhesion, has excellent resistance to water and corrosion prevention of, in Marine and other bad environment long-term protection up in action.
Second, purpose:

         the paint can be used as the outer wall of pipeline, underground pipeline corrosion, the outer wall of heat pipe outside wall, sea water or fresh water pipeline corrosion, outside wall face paint anticorrosion locks, but also can be used as waterproof, ChuLiChi cisterns, coal mine shaft and anticorrosive paint surface and derrick glass fiber cloth bandage, supporting the use of anti-corrosion performance is good.
Three, performance and technical parameters:
1, color:                                                      primer: brown;                 finish paint: black
2, density:                                                  primer: about 1.2 kg/L    finish paint: about 1.2 kg/L
3, flash point:                                             primer: 22 °C                   finish paint: 23 °C
4, theoretical usage:                                0.2 Okg/m2 (with 100 um dry film plan, not including loss) film thickness: dry film: 100 μ m
5, dry time:
 temperature          5 °C      20 °C          30 °C
Surface drying       8 h         4 h              2 h
The actual dry       48 h       24 h            16 h
6, the interval time:
temperature           5 °C      20 °C          30 °C
The shortest          48 h       24 h            16 h
The longest            7 d         5 d              2 d
7, matching:  the first part (paints) : a junior group b (curing agent) = 100:15 (weight ratio).
8, maturation period, party a and party b: two components mixed evenly, must be approved by age 30 min rear can use.
9, in25 °C: more than 8 h, use up in less than 5 °C should not be when construction.
Four, coating methods:

        brush, roller coating, air spray, high pressure without gas spraying all can
1 and nozzle diameter: (1) high pressure gas spray nozzle diameter is 0.4 0.5 mm; 

                                        (2) the nozzle diameter: 2.0-Omm
2, gushing pressure: (1) high pressure without gas spraying: 20-30 MPa;

                                    (2) air spray: 0.2 0.4 MPa.
3, thinner: 102 special thinner
4, amount of thinning: 0-10% (in paint weight plan)
Five, the preceding supporting coating:

        high-build coal tar epoxy anti-corrosion primer.
Six, that after supporting coating:

        high-build coal tar epoxy antiseptic surfaces.
Seven, surface treatment:

         primer directly applied in steel, 1, if have oxide skin, subject is shot or sandblasting processing, to Sweden Sa2.5 level standard rust. 2, such as no oxide skin, can is shot or sandblasting processing of Sweden derusting standard Sa2.5 level or pneumatic, electric tool grinding to Sweden St3 level standard derusting; In a shop primer coating surface are need to the second derusting will damage shop primer and dirt completely clear clean and polished to Sweden St3 level standard rust. Construction conditions: substrate temperature shall be above 3 °C above the dew point, relative humidity should be less than 85%. Construction substrate temperature below 5 °C epoxy firming agent and when to stop reaction, can't construction.
Eight, the storage period:

        12 months.
Nine, statement:

         the above this product information and data is according to our test and actual the experience of accumulating and can be used as a guide for construction. For we do not understand in the construction, our factory only guarantee that the quality of the paint itself, will not be responsible for other aspects. This specification, and we will be according to the continuous improvement of products shall have the right to make changes.