It is used for building,structures,basement,roofing,bridges,reservoirs, ponds, stands, kitchen,exterior waterproof works.
Introductionsingle composition water-based acrylic waterproof coating. It is made by taking pure acrylicemulsion and polyatomic polyacrylic acid emulsion as the basic materials and adding a variety of additives and inorganic fillers.After coating,elastic waterproof membrane with resilient property andstrong cohesive force can be formed, and a rigid-flexible joint ofcomplete waterproofing system shall be shaped on the substrate, so as to adapt to the various structural deformations and act as the function of long-term waterproof and impermeability. This product can be made as different colors.ApplicationsThis product is widely used for waterproof, moisture-proof, reconstruction and leak repairing of those parts, such as concrete roofing, wall, asbestos cement tile roofing, interior wall, bathroom and warehouse. It can also be used as protective coating of other waterproof layers.Featuressingle composition coating and easy to be constructed in short time.Property°CMain Performance
| Test item | Performance index | |
| Tensile strength(MPa) | ≥1.5 | |
| Elongation(%) | ≥300 | |
| Flexibility in low temperature(Φ10mm) | -20°C,No crack | |
| Water permeability(0.3MPa,30min) | No flooding | |
| Solid content | ≥65 | |
| Drying time (h) | Surface drying time | ≤4 |
| Total drying time | ≤8 | |
| Tensile strength conservation rate after processing (%) | Heat treatment | ≥80 |
| Alkali treatment | ≥60 | |
| Acid treatment | ≥40 | |
| Artificial weathering treatment | ≥80~150 | |
| Elongation ratio after processing (%) | Heat treatment | ≥200 |
| Alkali treatment | ≥200 | |
| Acid treatment | ≥200 | |
| Artificial weathering treatment | ≥200 | |
| Magnification ratio after heating (%) | Elongation | ≤1.0 |
| Shortening | ≤1.0 | |