LITONG CHEMICAL CO,LTD (FOSHAN & WUXI)
1) Product Ingredients
Adhensive solvent like high chlorination polyethylene, carbon shaping mediums like pentaerythritol, vesicants like melamine, catalyzers for carbon shaping, pigment ,additive, solvent, etc.
2) Usage of Product
Widely used for interior steel structure in large-scale constructiongs, such as exhibitions, airport lobbies, supermarkets, star hotels and workshops where fireproof and anticorrosion required.
3) Product Property & Technical Data
Testing item | Standard Clause | Technical data |
Fire-proof performance | GB149007-2002,5.2.16.6.66.5.7 | Thickness of coating:2.0mm±0.2mm:time of fireproofing:≥1.0h; Max roll degree of beam plate:≤Ln/20-281.5mm(Ln is the counting span for test samples) |
State in container | 5.2.1 | Even and exquisite after stirring, without agglomeration |
Drying Time(surface)/h | 5.2.1 | ≤8 |
Appearance and color | 5.2.1 | The appearance and color should have no obvious difference from the samples after the coating is dried |
Crack resistance initial drying stages | 5.2.1 | Cracks should not appear |
Adhension strength/Mpa | 5.2.1 | ≥0.20 |
Waterproof | 5.2.1 | ≥24,no rifting, no paint dropping, and no bubbles |
Cold and hot circulation resistance/time | 5.2.1 | ≥15, no rifting, no paint dropping, and no bubbles |
Paints | Environment condition | Thickness of dry film(micron) | Density | Way of | Mixing ratio | Time for drying | No. of coating | Preserved life(months) |
Chlorosulfonated polyethylene anticorrosion paints | General coating | 80-100 | 1.12 | Spray-coating brush coating | A:B=10:1 | Surface dry:0.5h Inner dry:24h | 3-4 | 12 |
Hydroxy-acid enamel paint | Decorative coating | 100-150 | 1.27 | Spray-coating brush coating | Single component | Surface dry:6h Inner dry:24h | 2-4 | 12 |
Organosilicon high temperature-resistant, anticorrosion paint | Chemicals-resist-antatmospheric coating | 100-140 | 1.23 | Spray-coating brush coating | A:B=100:2 | Surface dry:1h Inner dry:24h | 2-3 | 12 |
Anti-corrosion paint special for power plant spots | Acid,alkali,and salt-resistant chemistry medium coating | 150-220 | 1.12 | Spray-coating brush coating | A:B=18:3 | Surface dry:2h Inner dry:24h | 2-4 | 12 |
Paints for interior finished oil cans | Waterproof, oil-resistant coating | 140-180 | 1.45 | Spray-coating brush coating | A:B=11:15 | Surface dry:2h Inner dry:24h | 2-3 | 12 |
Chlorosulfonated polyethylene anticrack and anticorrosion paints | Anti-crack coating | 80-120`` | 1.21 | Spray-coating brush coating | A:B=10:1 | Surface dry:0.5h Inner dry:24h | 2-3 | 6 |
Anti-corrosion paints for Epoxyasphalt underground | Ocean moisture-resistant coating | 20-300 | 1.13 | Spray-coating brush coating | A:B=10:1 | Surface dry:2h Inner dry:24h | 2-4 | 12 |
Anti-cprrpsopm [aomts fpr gas canomet | Anti-corrosion coat gas cabinet | 150-200 | 1.15 | Spray-coating brush coating | A:B=10:1 | Surface dry:0.5h Inner dry:24h | 2-5 | 6 |
Damp-proof paint for cooling water tower | Cooling water tower interior coat | 150-180 | 1.18 | Spray-coating brush coating | A:B=10:1 | Surface dry:0.5h Inner dry:24h | 2-4 | 6 |