Double Coating Paints for Aluminum
Introduction: paints include Double Coating PE Paint and Double Coating PVDF Paint. Double Coating PE Paint covers anti-scratch paint, paint for aluminum composite panel and ceiling paint.
1) Anti-scratch paint: used for roller shutters;
2) Paint for aluminum composite panels: used for common architectural materials;
3)Paint for ceiling: used for ceiling and good flexibility materials;
4)PVDF paint: ued for superior aluminum composite panels, with its excellent weatherproof characteristics.
Testing item | Standard Clause | Technical data | ||||||
Fire-proof performance | GB149007-2002,5.2.16.6.66.5.7 | Thickness of coating:2.0mm±0.2mm:time of fireproofing:≥1.0h; Max roll degree of beam plate:≤Ln/20-281.5mm(Ln is the counting span for test samples) | ||||||
State in container | 5.2.1 | Even and exquisite after stirring, without agglomeration | ||||||
Drying Time(surface)/h | 5.2.1 | ≤8 | ||||||
Appearance and color | 5.2.1 | The appearance and color should have no obvious difference from the samples after the coating is dried | ||||||
Crack resistance initial drying stages | 5.2.1 | Cracks should not appear | ||||||
Adhension strength/Mpa | 5.2.1 | ≥0.20 | ||||||
Waterproof | 5.2.1 | ≥24,no rifting, no paint dropping, and no bubbles | ||||||
Cold and hot circulation resistance/time | 5.2.1 | ≥15, no rifting, no paint dropping, and no bubbles | ||||||
Environment condition | Thickness of dry film(micron) | Density | Way of | Mixing ratio | Time for drying | No. of coating | Preserved life(months) | |
Chlorosulfonated polyethylene anticorrosion paints | General coating | 80-100 | 1.12 | Spray-coating brush coating | A:B=10:1 | Surface dry:0.5h Inner dry:24h | 3-4 | 12 |
Hydroxy-acid enamel paint | Decorative coating | 100-150 | 1.27 | Spray-coating brush coating | Single component | Surface dry:6h Inner dry:24h | 2-4 | 12 |
Organosilicon high temperature-resistant, anticorrosion paint | Chemicals-resist-antatmospheric coating | 100-140 | 1.23 | Spray-coating brush coating | A:B=100:2 | Surface dry:1h Inner dry:24h | 2-3 | 12 |
Anti-corrosion paint special for power plant spots | Acid,alkali,and salt-resistant chemistry medium coating | 150-220 | 1.12 | Spray-coating brush coating | A:B=18:3 | Surface dry:2h Inner dry:24h | 2-4 | 12 |
Paints for interior finished oil cans | Waterproof, oil-resistant coating | 140-180 | 1.45 | Spray-coating brush coating | A:B=11:15 | Surface dry:2h Inner dry:24h | 2-3 | 12 |
Chlorosulfonated polyethylene anticrack and anticorrosion paints | Anti-crack coating | 80-120`` | 1.21 | Spray-coating brush coating | A:B=10:1 | Surface dry:0.5h Inner dry:24h | 2-3 | 6 |
Anti-corrosion paints for Epoxyasphalt underground | Ocean moisture-resistant coating | 20-300 | 1.13 | Spray-coating brush coating | A:B=10:1 | Surface dry:2h Inner dry:24h | 2-4 | 12 |
Anti-cprrpsopm [aomts fpr gas canomet | Anti-corrosion coat gas cabinet | 150-200 | 1.15 | Spray-coating brush coating | A:B=10:1 | Surface dry:0.5h Inner dry:24h | 2-5 | 6 |
Damp-proof paint for cooling water tower | Cooling water tower interior coat | 150-180 | 1.18 | Spray-coating brush coating | A:B=10:1 | Surface dry:0.5h Inner dry:24h | 2-4 | 6 |