carbon black
Minimum Order: 0
Quality/Safety Certification: 0.00
odine No. mg/g D1510 116.0 126.0
Oil Absorption, cc/100g D2414 108.0 120.0
Toluene Discolouration, % D1618 8.0 -
| Property | ASTM | MIN | MAX |
| Iodine No. mg/g | D1510 | 116.0 | 126.0 |
| Oil Absorption, cc/100g | D2414 | 108.0 | 120.0 |
| Toluene Discolouration, % | D1618 | 8.0 | - |
| Heat Loss, % | D1509 | - | 2.0 |
| Tint Strength vs IRB 3# | D3265 | 110.0 | 125.0 |
| Ash, % | D1506 | - | 0.8 |
| 325# Sieve Residue,% | D1514 | - | 0.100 |
| Density, lb/cu ft | D1513 | 20.0 | 24.0 |
| Fines 5 min, % | D1508 | - | 8.0 |
| 300% Modulus, vs IRB6 Mpa | D412 | -0.70 | 2.55 |
| Property | ASTM | MIN | MAX |
| Iodine No. mg/g | D1510 | 77.0 | 88.0 |
| Oil Absorption, cc/100g | D2414 | 95.0 | 105.0 |
| Toluene Discolouration, % | D1618 | 80 | - |
| Heat Loss, % | D1509 | - | 2.0 |
| Tint Strength vs IRB 3# | D3265 | 98.0 | 108.0 |
| Ash, % | D1506 | - | 0.8 |
| 325# Sieve Residue,% | D1514 | - | 0.100 |
| Density, lb/cu ft | D1513 | 21.5 | 25.0 |
| Fines 5 min, % | D1508 | - | 5.0 |
| Fines 20 min, % | D1508 | - | 8.0 |
| 300% Modulus, vs IRB6 Mpa | D412 | 0.14 | 2.90 |
| Property | ASTM | MIN | MAX |
| Iodine No. mg/g | D1510 | 38.0 | 48.0 |
| Oil Absorption, cc/100g | D2414 | 116.0 | 126.0 |
| Toluene Discolouration, % | D1618 | 80 | - |
| Heat Loss, % | D1509 | - | 2.0 |
| Ash, % | D1506 | - | 0.8 |
| 325# Sieve Residue,% | D1514 | - | 0.100 |
| Density, lb/cu ft | D1513 | 20.0 | 24.0 |
| Fines 5 min, % | D1508 | - | 8.0 |
| Fines 20 min, % | D1508 | - | 12.0 |
| 300% Modulus, vs IRB6 Mpa | D412 | 0.30 | 3.10 |
| Property | ASTM | MIN | MAX |
| Iodine No. mg/g | D1510 | 31.0 | 41.0 |
| Oil Absorption, cc/100g | D2414 | 85.0 | 95.0 |
| Toluene Discolouration, % | D1618 | 80 | - |
| Heat Loss, % | D1509 | - | 2.0 |
| Ash, % | D1506 | - | 0.8 |
| 325# Sieve Residue,% | D1514 | - | 0.100 |
| Density, lb/cu ft | D1513 | 24.0 | 28.0 |
| Fines 5 min, % | D1508 | - | 5.0 |
| Fines 20 min, % | D1508 | - | 8.0 |
| Pellet Crush Strength, avg g | D3313 | 10 | 50 |
| Pellet Crush Strength, max g | D3313 | - | 60 |
| 300% Modulus, vs IRB6 Mpa | D412 | -1.50 |