1.Low light transmission rate
2.High surface gloss,good reflective effect
3.Good lamination and printabity
4.Coated on side
Polyerter Film for General Purposes
Chracteristics:
1.Low light transmission rate
2.High surface gloss, a good reflective effect
3.Good lamination and printabity
4.Coating on one side corona,better for printing
Applications:
Suitable for the application with smooth and low light transmission requirement.
Specificatios:
Thickness | Width | Roll ID |
15~250μm | Customized | 76mm(3''),152mm(6'') |
Note:Other specifications are customized. | ||
Typical Physical Properties:
Items | Units | Typical Values | Testing Methods |
Thickness | μm | 50 | DIN53370 |
Tensile Strength(MD/TD) | MPa | 140/170 | ASTM D 882 |
Elongation at Break(MD/TD) | % | 150/100 | ASTM D 882 |
Shrinkage(MD/TD)150°C, 30min | % | 1.5/0 | ASTM D 1204 |
Haze | % | 20 | ASTM D 1003 |
Items | Units | Typical Values | Testing Methods | ||
Thickness | μm | 12 | 50 | 100 | DIN53370 |
Tensile Strength(MD/TD) | MPa | 220/220 | 210/210 | 210/210 | ASTM D 882 |
Elongation at Break(MD/TD) | % | 140/130 | 170/150 | 200/150 | ASTM D 882 |
Modulus(MD/TD) | MPa | 4400/4400 | 4000/4000 | 4000/4000 | ASTM D 882 |
Shinkage(MD/TD)150°C, 30min | % | 1.5/0.5 | 1.5/0.5 | 0.5/0.5 | ASTM D 1204 |
Haze | % | 3.0 | 3.5 | 4.5 | ASTM D 1003 |