PVC Jacket Compound for Cables and Wires
PVC Jacket Compound for Cables and Wires

Minimum Order: 0
Quality/Safety Certification: 0.00


PVC Jacket Compound for Cables and Wires
Best quality,Competitive price
ISO9001,SGS,14001 certificated
In line with UL,IEC,GB

        PVC Jacket Compound for wires and cables, based on PVC resin, is made into granula by mixing, plastification and granulation with adding plasticizer, stabilizing agent, pigment and etc. The products meet various special requirements, such as different hardness, UV stable, environment friend (RoHs, REACH, PAHs, chlorinated alkanes free,  phthalate free, and etc.), sub-shine and fog surface, low temperature resistant, PS/ABS transfer proof, rodent-repellent, termite-repellent, and transparent, and etc.

 

Properties Table

 

Item

Unit

Standard Value

J-70

JR-70

H-70

HR-70

JGD70

Tensile Strength

≥ MPa

20

19

17

16

22

Elongation at Break

≥   %

190

200

230

240

180

Impact Brittleness Temperature

   °C

-15

-20

-25

-30

-15

Volume Resistivity, at 20 oC

≥Ωm

2.0×1012

6.0×1011

6.0×109

4.0×109

5.0×1012

Volume Resistivity, at 70 oC

≥Ωm

    ---

   ---

   ---

   ---

   ---

Dielectric Strength

≥ MV/m

28

28

26

26

28

Hot Deformation

≤   %

60

65

65

65

65

Thermal Stability Time

at 200 oC

≥  min

60

60

60

60

80

Oxygen Index

≥  %

 30

30 

30

30 

   ---

Thermal Aging

 

 

 

 

 

 

Aging Temperature

   °C

100±2

100±2

100±2

120±2

135±2

Aging Time

     h

168

168

168

168

168

Variation on Tensile Strength

   %

2

4

5

5

0

Variation on Elongation at Break

   %

-8

-8

-10

-10

-5

Loss of Mass

g/m2

16

18

19

20

17

 

 For more informations, pls feel free to contact  us!

Ads by Google



About Us | Contact Us | Help | Terms & Conditions
Hot Products: A | B | C | D | E | F | G | H | I | J | K | L | M | N | O | P | Q | R | S | T | U | V | W | X | Y | Z | 0-9
Copyright Notice @ 2008-2022 B2BAGE Limited and/or its subsidiaries and licensors. All rights reserved.