pc solid sheet/polycarbonate sheet/polycarbonate solid sheet
1.any colors can be available
2.thinkness1.5-16mm
3.UV cut

Thickness	Standard Width	Length	Theoretical Weight	Standard Color
mm	mm	m	Kg/sq.m.
1.5		custom-made		For large order,
1.8			2.16
2.2			2.64
2.7			3.24
3		Size can be custom-made	3.60
3.5			4.20
4			4.80
5			6.00
6			7.20
7			8.40
8			9.60
9			10.80
10			12.00
11			13.20
12			14.40
13			15.60
14			16.80
15			18.00
16			19.20

PropertiesExperimental Condition
(American Customary System)ASTM Method (American
Society of Testing Materials)Unit--international System
(American Customary System)Values
(American Customary System)Physical propertyDensityD-1505g/cu.cm(lb/cu.ft)1.2(75)Water content24h,23°CD-570%0.15Mechanical propertyTensional yield10mm/min
(0.4in./min)D-638Mpa(psi)65(9400)Ultimate tensile strength10mm/min
(0.4in./min)D-638Mpa(psi)60(8800)Yield strain10mm/min
(0.4in./min)D-638%6Ultimate strain10mm/min
(0.4in./min)D-638%>90Stretching elastic coefficient10mm/min
(0.4in./min)D-638Mpa(psi)2000(290000)Bending coefficient1.3mm/min
(0.052in./min)D-790Mpa(psi)2600(380000)Bending force upon yielding1.3mm/min
(0.052in./min)D-790Mpa(psi)100(14500)Scrath-resistant load23°C(73°F)D-256J/m(ft.lbf/in.)800(15)Charpy impact load23°C(73°F)D-256J/m(ft.lbf/in.)800(15)Drop resistant abilityISO-6603/1BJ(ft.lbf)158(117)Rockwell hardnessD-785R scale/M scale125/75Thermal propertyLong-term service temperature°C(°F)-75~100(-175~212)Short-term service temperature°C(°F)-75~120(-175~250)Heating deviating temperature1.82MPa(264psi)D-648°C(°F)130(265)Vicat softening temperature1kg(2.2lb)D-1525°C(°F)150(300)Linear thermal expansion coefficientD-69610-5/°C(10-5°F)6.5(3.6)Thermo-conductivityC-177W/m°K(Btu-in./hr-ft.2-°F)0.21(1.46)Specific heat capacityC-351kJ/kg°K(Btu/lb°F)1.26(0.31)Optical performanceAmbiguityD-1003%<0.5LuminousnessD-1003%89Refraction rateD-5421.59Yellowing indexD-1925Notes:
1.he experiment condition,unit and experiment numerical values in thes table presented by American standard are listed between brackets.
2.The experiment results shown in this table are completely obtained in accordance with the experimental method of ASTM(American Society of Testing Materials),except for the results marked with "b",which is obtained by another experimental method.
3.The experimental results given in thes table are closest to the properties of sheets of thickness 3mm(1/8 inch)(if the results are to be applied).