1.Grade:Clear Polycarbonate Sheets
2.Thickness:0.25mm to 1.0mm .
3.Texture: polished/polished.
KLX PC-811A film is a polished/polished film and they are widely used for auto, electrical and electronic industries, LCD displays, mechanical elements, electroplate mirrors, various kinds of signs,membrane switches, nameplates and protection veils.
Grade | Color | Texture | Thickness (mm) | Width (mm) |
KLX PC-811A | Natural | Polished/Polished | 0.125-1.000 (0.004″-0.047″) | 915 & 930 & 1000 & 1230 (3’ & 3.27’ & 4′) |
Typical Property Values
Property | Item | Test Method | Unit | Standard Value |
Performance | Density | ASTM D792 | g/cm3 | 1.2 |
Absorption Rate,24hrs | ASTM D570 | % | 0.35 | |
| Light Transmission | ASTM 1003 | % | 89~93 | |
Haze | ASTM 1003 | % | <1 | |
Mechanical Performance | Tensile Strength | ASTM D882 ISO527 | PSI MPa | 8800 60 |
Tensile Elongation at Break | ASTM D882 | % | >100 | |
mpact Strength(0.75mm) | ASTM D3029 ISO 6603-1 | ft-Ib J | 23 31 | |
Tear Strength Propagation | ASTM D1922 | g/mil | >30 | |
Thermal Performance | Vicat Softening Temperature | ASTM D1525 | °C | 135 |
Shrinkage at 135°C | ASTM D1204 | % | <0.2 | |
Electrical Performance | Dielectric Strength(0.25mm) | ASTM D149 | V/mil | 1700 |
Surface Resistivity 25°C,50%RH | ASTM D257 | Ω | >1.0×1015 | |
Volume Resistivity 25°C,50%RH | ASTM D257 | Ω·cm | >1.0×1016 | |
UL Flammability | Film thickness ≥0.25 mm | UL BULLETIN 94 | UL94 | V-2 |
Film thickness <0.25 mm | VTM-2 |