T&P PVC waterproof flash tape
1)aging resistance
2)UV rays resistance
3)High tensile strength
4)long service life
T e l:(86)-536-5269708
E m a i l:mingqun0536%y a h o o.c o m.c n
mingqun021206%163.c o m
Skyp:mingqun0536
Features:
1)Exposed to sunshine: UV rays resistance, long service life and aging resistance
2)Easy installation and dimensional stability: can be wieldable under wide range of temperature and experience minus dimensional change in thermal treatment
3)High tensile strength and elongation thus can accommodate movements of substrates
4)Good flexibility under low temperature, good adaptability to ambient temperature difference
5)Secure anti-puncture and good rooting resistance, no pollution caused to environment when being welded and good waterproofing choice for plant roofs
6)Good plasticity: convenient and fast treatment of detailed parts of corners and edges
7)3 meters width reduce the joints and help saving materials or labor cost
Long Lige Fire Resistance Root and Resistance Elasticity
UV-Resistance Hot Air Welding Chemical Resistance Tensile Strengt
Available size
Thickness(mm) | Width(mm) | Length(m) |
1.2 | 100/150/200 | 15 or 20/roll |
1.5 | 100/150/200 | 15 or 20/roll |
2.0 | 100/150/200 | 15 or 20/roll |
Note: Other sizes can be offered upon specific requirements |
Specification
No. | ITEM | I | II | |
1 | Tension strength / Mpa | 8.0 | 12.0 | |
2 | Fracture elongation ≥ / % | 200 | 250 | |
3 | Measurement changing at heating / % | 3.0 | 2.0 | |
4 | Cold bending | -20°C no leaking | -25°C no leaking | |
5 | Perforation resistance | Water impermeability | ||
6 | Water impermeabvilitv | Water impermeability | ||
7 | Binding property with cutting(N/mm) | Appearance | 3.0/breaking membrane | |
8 | Hot air ageing | Appearance | No craze,nobubble,nocohering,hole | |
Tension strength / % | ±25 | ±20 | ||
Fracture elongation changing rate | ||||
Cold bending / % | -15°C no leaking | -20°C no leaking | ||
9 | Chemistry corrosion resistance | Tension strength / % | ±25 | ±20 |
Fracture elongation changing rate | ||||
Cold bending / % | -15°C no leaking | -20°C no leaking | ||
10 | Phytotrons acceleratingageing | Tension strength / % | ±25 | ±20 |
Fracture elongation changing rate | ||||
Cold bending / % | -20°C no leaking | -20°C no leaking |