E316-16 is a low carbon stainless steel electrode with titanium calcium type coating .
Description:E316-16 is a low carbon stainless steel electrode with titanium calcium type coating .As the deposited mental contains Mo, it has good resistant properties against heat, corrosion ,and crack, especially against the corrosion of chlorine ion. It is used on both AC and DC and has good manipulate properties.
Application:Used to weld 0chrome 18 Nickel 12 Mo2 stainless steel structure worked in the medium of organic acid and inorganic acid(not oxidizing acid), or weld heterogeneity steel structure.
CHEMICAL COMPOSITION OF MELTING METAL(%)
C | Mn | Si | Cr | Ni | Mo | Cu | S | P |
≤0.08 | 0.5~2.5 | ≤0.90 | 17.0~20.0 | 11.0~14.0 | 2.0~3.0 | ≤0.75 | ≤0.030 | ≤0.040 |
Reference Current
Diameter(mm) | 2.5 | 3.2 | 4.0 | 5.0 |
Current | 50~80 | 80~110 | 110~160 | 160~200 |
Note:
Before welding ,the electrode must be baked at about 150 degree centigrade for one hour. It should be used on DC possibly, not too large current otherwise electrode becomes red easily. The melting depth is lower when used AC.