MEPR-g-MAH-1 is produced by grafting EPDM with maleic anhydride in the extruding machine.
1Description:
MEPR-g-MAH-1 is produced by grafting EPDM with maleic anhydride in the extruding machine. Because of the introduction of strong polar side groups to the non-polar main polymer chain, excellent compatibility can be achieved between MEPR-g-MAH-1 and polar resin.
The typical appliance of MEPR-g-MAH-1:
(1) The flexibilizer of nilon, to improve the impact resistance;
(2) The compatibilizer and flexibilizer of polypropylene/nilon composite;
(3) The flexibilizer of other polar resin.
The appearance of MEPR-g-MAH-1:
Light yellow resin particle which can flow freely.
Nature:
Items | Test Methods | Unit | Test Result |
Density | GB1033-86 | g/cm2 | 0.875 |
Meny Viscosity (ML1+4,100) | GB1323.1-2000 |
| 42 |
Graft Ratio | Acid-base titration | % | 0.90 |
*The data above is the typical ones of MEPR-g-MAH-1 after the test, not the warranty ones of our firm. | |||
Usage:
MEPR-g-MAH-1 has high graft ratio of maleic anhydride and excellent elastic behavior. As a result, adding a small amount of MEPR-g-MAH-1 can bring ideal result. On average, the added amount is 2-15%. The specific amount depends on the users demand on the quality of the product and the applied system. To achieve the optimum result, the processing facility and technology should make sure that the MEPR-g-MAH-1 can disperse well in the system.
Packaging:
In 25kg kraft bags lined with PP. Stored in shady, cool and dry places.