Modified polymeric resins, engineering plastics, engineering plastics (PBT Series), PBT series modified polymeric resins
Modified polymeric resins, engineering plastics, engineering plastics (PBT Series), PBT series modified polymeric resins
The engineering plastics (PBT Series)include Fiberglass reinforced, Flame retarded, Flame retarded & Reinforced.
The technical data and applications of Fiberglass reinforced:
a) Tensile strength at break: >90
b) Bending strength (Mpa) ASTMD790: >120
c) Flexural modulus(Mpa) ASTMD790: >7000
d) Impact strenth/J.m-1(notch) ASTMD256: >70
e) Shrinkage ratio (%) ASTMD955: <0.5
Applications: Electrical appliance parts, car door pulls, bolts
The technical data and applications of flame retarded:
a) Tensile strength at break: >40
b) Bending strength (Mpa) ASTMD790: >80
c) Flexural modulus(Mpa) ASTMD790: >2000
d) Impact strenth/J.m-1(notch) ASTMD256: >40
e) Shrinkage ratio (%) ASTMD955: <0.5
f) Combustibility: 1.6mm Glass HB
Applications: Linker, relays, junction boxes, switches.
The technical data and applications of flame retarded & reinforced:
a) Tensile strength at break: >90
b) Bending strength (Mpa) ASTMD790: >120
c) Flexural modulus(Mpa) ASTMD790: >7000
d) Impact strenth/J.m-1(notch) ASTMD256: >70
e) Shrinkage ratio (%) ASTMD955: <0.5
f) Combustibility: 1.6mm Glass HB
Applications: Linker, relays, power switches, winding framework, jacks, fans, light parts.