reinforced with GF 30% & mineral powder PA6 nylon6 plastic
Minimum Order: 0
Quality/Safety Certification: 0.00
PA6 with GF & mineral powder
mineral powder
with 43% GF
reinforced
PA6 with GF & mineral powder
we are a factory which mainly produces flame-redundant nylon series products which are anti-high-temperature, environment-friendly, and of high strength and technology content. they are now widely used in various newly-emerging fields, including automobile, communication, electronics, electrical appliance, household appliance and sports products etc.
| Performance | Test condition | Testing standard | Units | BZ425 |
| Mechanical property | ||||
| Tensile strength | 5mm/min | ISO527-1/2 | Mpa | 115 |
| Elongation at break | 5mm/min 50mm/min | ISO527-1/2 | % | 1.6 |
| Bending modulus | 2mm/min | ISO178 | Mpa | 6800 |
| Bending strength | 2mm/min | ISO178 | Mpa | 190 |
| Charpy notched impact strength | 23°C | ISO179/leA | KJ/m2 | 7.5 |
| Charpy unnotched impact strength | 23°C | ISO179/leA | KJ/m2 | 40 |
| Thermal | ||||
| Melting | DSC.10K/min | ISO3146 | °C | 225 |
| Heat distortion temp. A | 1.8Mpa | ISO75 | °C | 205 |
| Heat distortion temp. B | 0.45Mpa | ISO75 | °C | 215 |
| Electrical property | ||||
| Surface resistivity | IEC60093 | Ohm | 1/0.1 | |
| Volume resistivity | IEC60093 | Ohm×cm | 10/0.1 | |
| Anti-arc-track of | TestotutionA | IEC60012 | V | |
| Physical property | ||||
| Density | 23°C | ISO1183 | g/cm3 | |
| Hygroscopicity | 23°C,50%r.h | ISO62 | % | 0.8 |
| Absorbent/water absorption | 23°C /saturtion | ISO62 | % | 0.53 |
| Radial shrinkage | flow | ISO294-4 | % | 0.24 |
| Transverse shrinkage | transverse | ISO294-4 | % | |
| Flame retardant | ||||
| Flammability test | 1.6/3.0mm | |||
| The level of flame-retardant test | 1mm thickness | UL94 | ||
| Material description | PA6+43%GF powdered ore | |||